QuFe19 TIG Filler Wire Heat-Resistant 12 % Cr Steel 1.4922 / 1.4923 – up to 650 °C
QuFe19 TIG Filler Wire Heat-Resistant 12 % Cr Steel 1.4922 / 1.4923 – up to 650 °C
QuFe19 is the repair wire for heat-resistant, temperable 12 % Cr steels: DIN EN ISO 21952-A G/W CrMoWV12Si · AWS A5.9 ~ER505 · filler material no. 1.4937. Service temperature up to 650 °C.
It is matching to base materials 1.4922, 1.4923 and 1.4935 — the steels of turbine, boiler and power plant construction. The weld metal is temperable and hardenable (45–48 HRC) and can be textured, polished and chrome-plated. Mind the heat control: the material is martensitic, so pre-heating and controlled cooling are part of the process.
Recommended base materials
- 1.4922 (X20CrMoV11-1), 1.4923 (X22CrMoV12-1)
- 1.4935, 1.4926
- 1.4913, 1.4931
- Matching and similar heat-resistant 12 % Cr steels
Typical applications
- Modifications and repairs on heat-resistant 12 % Cr components
- Turbine and power plant construction
- Components with service temperature up to 650 °C
- Tools whose weld metal is later textured or chrome-plated
Properties and advantages
- Service temperature up to 650 °C — matching 1.4922 / 1.4923
- 45–48 HRC, Re 590 MPa · Rm 700 MPa · A 15 %
- Weld metal temperable and hardenable, texturable, polishable, chrome-platable, nitridable
- Alloyed with W and V for hot strength
TIG advantage: For larger deposit areas on cast and forged parts.
TIG welding wire packaging: 1,000 mm rod, 1 kg cardboard tube, 5 kg carton ,Ø 1.0 – 3.2 mm.
Material analysis (wt.-%)
C 0.21 | Si 0.4 | Cr 11.1 | Mn 0.6 | Mo 0.90 | V 0.3 | W 0.45 | Fe balance
Download
| Achievable hardness: | 45 - 48 HRC |
|---|---|
| Diameter: | 1,0 mm, 1,2 mm, 2,0 mm, 2,4 mm |
| Recommendations for basis material: | 1.4913, 1.4922, 1.4923, 1.4926, 1.4931, 1.4935 |
| Refinish: | chrome-plated , erodible , Hardenable , nitridable , Observe heat conduction , polishable, remunerable , structurable |
| Rod length: | 1000 mm |
Related products
QuFe19 is the repair wire for heat-resistant, temperable 12 % Cr steels: DIN EN ISO…
QuFe10 is the standard filler metal for modifying and repairing mould cavities in the…
QuFe10Cr is the CrMo-alloyed variant for highly stressed mould cavities in the tempered…
QuFe10NiMo is the NiMo-alloyed variant for modifying and repairing mould cavities — and,…
QuFe15 is a CrMo2-alloyed filler metal for modifying and repairing mould cavities in the…
QuFe15 is a CrMo2-alloyed filler metal for modifying and repairing mould cavities in the…
QuP20 is the wire for mould steel AISI P20 (~1.2311) — and its distinguishing feature is…
QuFe10 is the standard filler metal for modifying and repairing mould cavities in the…