QuP20 Rod – Laser Welding Wire Mould Steel P20 / 1.2311 – 38–46 HRC, Etchable and Grainable
€145.18
QuP20 Rod – Laser Welding Wire Mould Steel P20 / 1.2311 – 38–46 HRC, Etchable and Grainable
QuP20 is the wire for mould steel AISI P20 (~1.2311) — and its distinguishing feature is stated literally in the datasheet header: post-processing by etching and texturing.
The deposit is EDM-machinable, texturable, polishable, chrome-platable, etchable, nitridable, temperable and hardenable. If you repair a cavity that is subsequently photo-etched or grained, that is exactly what you need — many harder build-up wires are ruled out at this point. At 38–46 HRC it is well above QuFe10Cr (27–38 HRC) and usable in long-term service up to 570 °C.
Recommended base materials
- 1.2311 (AISI P20), 1.2312, 1.2738
- 1.2162, 1.2764, 1.2767
- 42CrMo4 / AISI 4140, 25CrMo4, AISI 4130
- 13CrMo 4 4, GS-17 CrMo5 5
Typical applications
- Mould cavities that are subsequently etched or grained
- Photo-etching and texturing
- Heavily loaded plastic moulds
- Components in long-term service up to 570 °C
Properties and advantages
- Etchable and texturable — photo-etching and graining possible
- 38–46 HRC
- EDM-machinable, polishable, chrome-platable, nitridable, temperable, hardenable
- Long-term service up to 570 °C. Re >480 · Rm >570 MPa · A >22 %
Rod form: Rod lengths 1000 mm and 333 mm, Ø 0,3 mm – 0,6 mm.
Material analysis (wt.-%)
C 0.36 | Si 0.50 | Mn 0.80 | Cr 1.70 | Mo 0.40 | Fe balance
Download
| Achievable hardness: | 38 - 46 HRC |
|---|---|
| Diameter: | 0,3 mm, 0,4 mm, 0,5 mm, 0,6 mm |
| Recommendations for basis material: | 1.2162, 1.2311, 1.2312, 1.2738, 1.2764, 1.2767, 13CrMo 4 4, 25CrMo4, 42CrMo4, AIS4130, AISI4130, AISI4140, GS-17 CrMo5 5 |
| Refinish: | Hardenable , chrome-plated , erodible , etable , nitridable , polishable, remunerable , structurable |
| Rod length: | 333 mm, 1000 mm |
| Wire: | Laser welding wire |
Related products
QuP20 is the wire for mould steel AISI P20 (~1.2311) — and its distinguishing feature is…
QuFe10Cr is the CrMo-alloyed variant for highly stressed mould cavities in the tempered…
QuFe10Cr is the CrMo-alloyed variant for highly stressed mould cavities in the tempered…
QuFe10Cr is the CrMo-alloyed variant for highly stressed mould cavities in the tempered…
QuLPA-Fe10Cr is the laser cladding powder for heavily loaded mould cavities. It matches…
QuFe10 is the standard filler metal for modifying and repairing mould cavities in the…
QuFe10NiMo is the NiMo-alloyed variant for modifying and repairing mould cavities — and,…