QuMed4009 Rod – Laser Welding Wire 13 % Cr Steel / ER410 (1.4009)

QuMed4009 is a martensitic 13 % chromium steel to EN ISO 14343-A G/W 13 · AWS A5.9 ER410 (filler material no.: ~1.4009). Unlike the austenitic wires of the QuMed range, this weld metal hardens on cooling — it is a quench-and-temper material, not an austenite.The wire is intended for components that need corrosion resistance in water, gas and steam atmospheres, and for build-ups on unalloyed and low-alloy steels up to 450 °C. The weld metal is readily polishable and machinable, hardness as welded 150–225 HB.Recommended base materials1.4000, 1.4006, 1.4008 — martensitic 13 % Cr steelsAISI 410, AISI 420 — the corresponding US gradesBuild-ups on 1.2083 and 1.2085Build-ups on unalloyed and low-alloy steels up to 450 °CTypical applicationsStructural parts in water, gas and steam atmospheresBuild-ups on tool steels 1.2083 / 1.2085Components that are subsequently polishedRepairs on martensitic 13 % Cr componentsProperties and advantagesReadily polishable and machinable — the repair can be finished cleanlyCorrosion-resistant in water, gas and steamHardness as welded 150–225 HBWeld metal: Re 380 MPa · Rm 550 MPa · A 15 %Bobbin form: K125, K250, K80, MA125, SH253 — wire weight 100 g–500 g, Ø 0,2 mm – 0,6 mm. Material analysis (wt.-%)C 0.08 | Si 0.6 | Mn 0.65 | Cr 13.0 | Ni 0.4 | Fe balance

QuFe18 is the martensitic 13 % Cr wire for general mechanical and plant engineering: AWS ER410 · ~1.4009.It is a hardenable material — it hardens as it cools. That is the decisive difference from the austenitic stainless wires: here you preheat and cool slowly rather than keeping things cold. In return you get a deposit that polishes and machines well and can afterwards be tempered to service hardness — the classic combination for valves, shafts, pump parts and sealing faces.Recommended base materials1.4000, 1.4006, 1.4008 — martensitic 13 % Cr steelsAISI 410, AISI 420 — the corresponding US gradesBuild-ups on 1.2083 and 1.2085Build-ups on unalloyed and low-alloy steels up to 450 °CTypical applicationsValves and sealing facesShafts and bearing seatsPump and turbine componentsRepairs on martensitic Cr steels in mechanical engineeringProperties and advantagesReadily polishable and machinable — the repair can be finished cleanlyCorrosion-resistant in water, gas and steamHardness as welded 150–225 HBWeld metal: Re 380 MPa · Rm 550 MPa · A 15 %Rod form advantage: Ideal for manual build-up welding with constant wire feed — also in hard-to-reach areas.Rod form: Rod lengths 1000 mm and 333 mm, Ø 0,2 mm – 0,8 mm. Material analysis (wt.-%)C 0.08 | Si 0.6 | Mn 0.65 | Cr 13.0 | Ni 0.4 | Fe balance

QuFe18 is the martensitic 13 % Cr wire for general mechanical and plant engineering: AWS ER410 · ~1.4009.It is a hardenable material — it hardens as it cools. That is the decisive difference from the austenitic stainless wires: here you preheat and cool slowly rather than keeping things cold. In return you get a deposit that polishes and machines well and can afterwards be tempered to service hardness — the classic combination for valves, shafts, pump parts and sealing faces.Recommended base materials1.4000, 1.4006, 1.4008 — martensitic 13 % Cr steelsAISI 410, AISI 420 — the corresponding US gradesBuild-ups on 1.2083 and 1.2085Build-ups on unalloyed and low-alloy steels up to 450 °CTypical applicationsValves and sealing facesShafts and bearing seatsPump and turbine componentsRepairs on martensitic Cr steels in mechanical engineeringProperties and advantagesReadily polishable and machinable — the repair can be finished cleanlyCorrosion-resistant in water, gas and steamHardness as welded 150–225 HBWeld metal: Re 380 MPa · Rm 550 MPa · A 15 %Bobbin form: K125, K250, K80, MA125, SH253 — wire weight 100 g–500 g, Ø 0,2 mm – 0,8 mm. Material analysis (wt.-%)C 0.08 | Si 0.6 | Mn 0.65 | Cr 13.0 | Ni 0.4 | Fe balance

QuLPA-Fe18 is the cladding powder made of martensitic 13 % Cr steel: ~EN ISO 14343-A G/W (13) · ~AWS A5.9 ER420 · material no. ~1.4028.It is intended for build-ups on structural parts in water, gas and steam atmospheres — wherever corrosion resistance is required alongside wear protection. Base materials are the 13 % martensitic Cr steels 1.4000–1.4006 / AISI 410 / AISI 420. On unalloyed and low-alloy steels it can be used up to 450 °C. The deposit polishes well, 55 HRC.Recommended base materials1.4000 – 1.4006 — martensitic 13 % Cr steelsAISI 410, AISI 420Build-ups on steels such as 1.2083, 1.2085Unalloyed and low-alloy steels up to 450 °CTypical applicationsStructural parts in water, gas and steam atmospheresComponents needing wear protection and corrosion resistance at oncePolished functional surfacesArea cladding by laser metal deposition (LMD)Properties and advantages55 HRC as depositedCorrosion resistant — 13 % chromiumGood polishing and machining behaviourGrain size 45–90 µmPowder form: for laser metal deposition (LMD). Material analysis (wt.-%)C 0.22 | Si 0.50 | Mn 1.20 | Cr 13.00 | Fe balance

QuNi40 is the titanium-alloyed nickel wire: EN ISO 18274 S Ni 2061 (NiTi3) · AWS A5.14 ERNi-1 · filler material no. 2.4155.The 3.3 % titanium is what sets it apart from the pure QuNi29. Titanium binds nitrogen and thus suppresses porosity — precisely what is needed for nickel-to-steel dissimilar joints and for repairs on grey cast iron (GG-GJL), where gases migrate from the base material into the weld pool. For matching pure-nickel joints without such influence, QuNi29 is the simpler alternative.Recommended base materials2.4060, 2.4061, 2.4066, 2.4068Commercial pure nickel grades, LC nickelNickel-clad steelsNickel-to-steel dissimilar jointsCast iron (GG-GJL) — repairs possible to a limited extentTypical applicationsPressure vessel and plant construction, chemical industryNickel-to-steel dissimilar jointsGrey iron repairs (GJL)Food industry, energy sectorProperties and advantagesTi 3.3 % — binds nitrogen, suppresses porositySuitable for nickel-to-steel dissimilar jointsGrey iron repairs possible to a limited extentWeld metal: Re 300 MPa · Rm 450 MPa · A 25 %Rod form advantage: Constant wire feed for manual repair welding, also on cast components.Rod form: Rod lengths 1000 mm and 333 mm, Ø 0,2 mm – 0,8 mm. Material analysis (wt.-%)C 0.02 | Si 0.3 | Mn 0.3 | Fe 0.1 | Ti 3.3 | Ni balance

QuFe66 is suitable for build-up welding on construction parts in water, gas and steam atmospheres and similar 17 % martensitic chrome steels where corrosion resistance is required. The weld can be easily polished. The material can be applied to non-alloy and low-alloyed steels up to a temperature of 450°C.Material analysisC: 0,08 | Si: 0,75 | Mn: 0,7 | Ni: 0,2 | Cr: 17,5

QuNi40 is the titanium-alloyed nickel wire: EN ISO 18274 S Ni 2061 (NiTi3) · AWS A5.14 ERNi-1 · filler material no. 2.4155.The 3.3 % titanium is what sets it apart from the pure QuNi29. Titanium binds nitrogen and thus suppresses porosity — precisely what is needed for nickel-to-steel dissimilar joints and for repairs on grey cast iron (GG-GJL), where gases migrate from the base material into the weld pool. For matching pure-nickel joints without such influence, QuNi29 is the simpler alternative.Recommended base materials2.4060, 2.4061, 2.4066, 2.4068Commercial pure nickel grades, LC nickelNickel-clad steelsNickel-to-steel dissimilar jointsCast iron (GG-GJL) — repairs possible to a limited extentTypical applicationsPressure vessel and plant construction, chemical industryNickel-to-steel dissimilar jointsGrey iron repairs (GJL)Food industry, energy sectorProperties and advantagesTi 3.3 % — binds nitrogen, suppresses porositySuitable for nickel-to-steel dissimilar jointsGrey iron repairs possible to a limited extentWeld metal: Re 300 MPa · Rm 450 MPa · A 25 %Bobbin form: K125, K250, K80, MA125, SH253 — wire weight 100 g–500 g, Ø 0,2 mm – 0,8 mm. Material analysis (wt.-%)C 0.02 | Si 0.3 | Mn 0.3 | Fe 0.1 | Ti 3.3 | Ni balance