QuFe11 TIG Welding Wire – Hot-Work Steel 1.2367 / 1.2343 – 38–42 HRC
QuFe11 TIG Welding Wire – Hot-Work Steel 1.2367 / 1.2343 – 38–42 HRC
QuFe11 is a build-up wire for hot-work tools: DIN EN 14700 S Fe 13, filler material no. 1.2367. The weld metal reaches 38–42 HRC and combines hot-wear resistance with toughness.
That combination is the whole point of this wire: components exposed at elevated temperature to impact, pressure and abrasion at the same time need weld metal that is not merely hard but also yields without cracking. For a harder, more temper-resistant build-up, use its sibling QuFe12 (42–48 HRC).
Recommended base materials
- 1.2343, 1.2344 (X38CrMoV5-1 / X40CrMoV5-1)
- 1.2367 (X38CrMoV5-3)
- 1.2606
- 1.2764 – 1.2767
Typical applications
- Forging dies
- Die-casting moulds and plastic moulds
- Guides and containers (extrusion)
- Continuous casting rolls
Properties and advantages
- 38–42 HRC — depending on machining and number of layers
- Hot-wear resistant and tough — for impact, pressure and abrasion at elevated temperature
- Weld metal can be hardened and tempered, nitrided, chrome-plated, CVD-coated
- Polishable and machinable
TIG advantage: For larger build-up areas where laser fine welding would be too slow. Ø 1.0–3.2 mm.
TIG form: for manual repair welding.
Material analysis (wt.-%)
C 0.1 | Si 0.4 | Mn 0.6 | Cr 6.5 | Mo 3.3 | Fe balance
Download
| Achievable hardness: | 38 - 42 HRC |
|---|---|
| Diameter: | 1,0 mm, 1,2 mm, 1,6 mm, 2,0 mm, 2,4 mm, 3,2 mm |
| Recommendations for basis material: | 1.2343, 1.2344, 1.2367, 1.2606, 1.2764, 1.2765, 1.2766, 1.2767 |
| Refinish: | CVD-coatable , chrome-plated , machinable , nitridable , polishable, remunerable |
| Rod length: | 1000 mm |
| Wire: | WIG wire |
Related products
QuFe11 is a build-up wire for hot-work tools: DIN EN 14700 S Fe 13, filler material no.…
QuFe11 is a build-up wire for hot-work tools: DIN EN 14700 S Fe 13, filler material no.…
QuFe21 is a high wear-resistance hardfacing wire to DIN EN 14700 S Fe 6 for tools exposed…
QuFe12 is the hard, temper-resistant build-up wire for hot-work tools: EN 14700 S Fe 3 ·…
QuFe21 is a high wear-resistance hardfacing wire to DIN EN 14700 S Fe 6 for tools exposed…
QuFe21 is a high wear-resistance hardfacing wire to DIN EN 14700 S Fe 6 for tools exposed…
QuFe12 is the hard, temper-resistant build-up wire for hot-work tools: EN 14700 S Fe 3 ·…