QuMed4571 Bobbin – Laser Welding Wire 1.4571 / 316Ti
€55.93
QuMed4571 Bobbin – Laser Welding Wire 1.4571 / 316Ti
QuMed4571 is a high-purity, titanium-stabilized stainless steel laser welding wire designed for medical technology. The material 1.4571 (X6CrNiMoTi17-12-2 / AISI 316Ti) combines the excellent corrosion resistance of the 316L family with reliable protection against intergranular corrosion through titanium stabilization — ideal for demanding weld joints without solution annealing.
Recommended base materials
- 1.4571 — X6CrNiMoTi17-12-2 / AISI 316Ti
- 1.4401 — X5CrNiMo17-12-2 / AISI 316
- 1.4404 — X2CrNiMo17-12-2 / AISI 316L
Typical applications
- Surgical instruments, endoscopy components
- Dental technology and dental implant repair
- Pharmaceutical and food-grade equipment (CIP/SIP-resistant)
- Corrosion-resistant build-up welding in the chemical industry
Advantages over 1.4404
- Titanium stabilization prevents intergranular corrosion at weld seams
- Increased high-temperature strength up to approx. 550 °C
- Suitable for demanding repair and build-up welding
Bobbin form: K125, K250, K80, MA125, SH253 — wire weight 100 g–500 g, Ø 0,2 mm – 0,8 mm.
Material analysis (wt.-%)
C ≤ 0.08 | Si ≤ 1.0 | Mn ≤ 2.0 | Cr 16.5–18.5 | Ni 10.5–13.5 | Mo 2.0–2.5 | Ti ≥ 5×C
Download
| Bobbin size: | K80, K125, K250, MA125, SH253 |
|---|---|
| Bobbin weight: | 100 g, 200 g, 500 g |
| Diameter: | 0,2 mm, 0,3 mm, 0,4 mm, 0,5 mm, 0,6 mm, 0,8 mm |
| Recommendations for basis material: | 1.4401, 1.4404, 1.4571 |
| Wire: | Dental & medical wire, Laser welding wire |
Related products
QuMed4576 is a high-purity, titanium-stabilized stainless steel laser welding wire designed for medical technology. The material 1.4571 (X6CrNiMoTi17-12-2 / AISI 316Ti) combines the excellent corrosion resistance of the 316L family with reliable protection against intergranular corrosion through titanium stabilization — ideal for demanding weld joints without solution annealing.Recommended base materials1.4571 — X6CrNiMoTi17-12-2 / AISI 316Ti1.4401 — X5CrNiMo17-12-2 / AISI 3161.4404 — X2CrNiMo17-12-2 / AISI 316LTypical applicationsSurgical instruments, endoscopy componentsDental technology and dental implant repairPharmaceutical and food-grade equipment (CIP/SIP-resistant)Corrosion-resistant build-up welding in the chemical industryAdvantages over 1.4404Titanium stabilization prevents intergranular corrosion at weld seamsIncreased high-temperature strength up to approx. 550 °CSuitable for demanding repair and build-up weldingBobbin form: K125, K250, K80, MA125, SH253 — wire weight 100 g–500 g, Ø 0,3 mm – 0,8 mm. Material analysis (wt.-%)C ≤ 0.08 | Si ≤ 1.0 | Mn ≤ 2.0 | Cr 16.5–18.5 | Ni 10.5–13.5 | Mo 2.0–2.5 | Ti ≥ 5×C
QuMed4571 is a high-purity, titanium-stabilized stainless steel laser welding wire designed for medical technology. The material 1.4571 (X6CrNiMoTi17-12-2 / AISI 316Ti) combines the excellent corrosion resistance of the 316L family with reliable protection against intergranular corrosion through titanium stabilization — ideal for demanding weld joints without solution annealing.Recommended base materials1.4571 — X6CrNiMoTi17-12-2 / AISI 316Ti1.4401 — X5CrNiMo17-12-2 / AISI 3161.4404 — X2CrNiMo17-12-2 / AISI 316LTypical applicationsSurgical instruments, endoscopy componentsDental technology and dental implant repairPharmaceutical and food-grade equipment (CIP/SIP-resistant)Corrosion-resistant build-up welding in the chemical industryAdvantages over 1.4404Titanium stabilization prevents intergranular corrosion at weld seamsIncreased high-temperature strength up to approx. 550 °CSuitable for demanding repair and build-up weldingRod form: Rod lengths 1000 mm and 333 mm, Ø 0,2 mm – 0,8 mm. Material analysis (wt.-%)C ≤ 0.08 | Si ≤ 1.0 | Mn ≤ 2.0 | Cr 16.5–18.5 | Ni 10.5–13.5 | Mo 2.0–2.5 | Ti ≥ 5×C
QuMed4576 is a high-purity, titanium-stabilized stainless steel laser welding wire designed for medical technology. The material 1.4571 (X6CrNiMoTi17-12-2 / AISI 316Ti) combines the excellent corrosion resistance of the 316L family with reliable protection against intergranular corrosion through titanium stabilization — ideal for demanding weld joints without solution annealing.Recommended base materials1.4571 — X6CrNiMoTi17-12-2 / AISI 316Ti1.4401 — X5CrNiMo17-12-2 / AISI 3161.4404 — X2CrNiMo17-12-2 / AISI 316LTypical applicationsSurgical instruments, endoscopy componentsDental technology and dental implant repairPharmaceutical and food-grade equipment (CIP/SIP-resistant)Corrosion-resistant build-up welding in the chemical industryAdvantages over 1.4404Titanium stabilization prevents intergranular corrosion at weld seamsIncreased high-temperature strength up to approx. 550 °CSuitable for demanding repair and build-up weldingRod form: Rod lengths 1000 mm and 333 mm, Ø 0,2 mm – 0,8 mm. Material analysis (wt.-%)C ≤ 0.08 | Si ≤ 1.0 | Mn ≤ 2.0 | Cr 16.5–18.5 | Ni 10.5–13.5 | Mo 2.0–2.5 | Ti ≥ 5×C
QuFe44 is suitable for joining stainless steel and heat resistant steels, non-corrosive build-up welding for e.g. apparatus and components for the food industry, chemical industry, textile and fuel industry.Material analysis C: 0,02 | Si: 0,85 | Mn: 1,8 | Cr: 18,5 | Ni: 12,5 | Mo: 2,6
QuMed4430 is suitable for joint welding of nonrusting and heat resistant steels. Corrosion-resistant joint weldings for instruments and building elements of the food industry, chemical industry, textile and fuel industry. For operating temperatures from -196°C up to +400°C.Material analysis C: 0,02 | Si: 0,85 | Mn: 1,8 | Cr: 18,5 | Ni: 12,5 | Mo: 2,6
QuFe50 is used for joint and build-up welding on stabilized, similar type chemical resistant CrNiMo-steels, found in chemical vessels and apparatus constructions for uses at temperatures between -196°C and +400°C.Material anaylsis C: 0,03 | Si: 0,4 | Mn: 1,5 | Cr: 19,0 | Ni: 12,0 | Mo: 3,0 | Nb: 0,55 | Fe: Rest